240 WHITE CLAY - Cone 6 (Photo C/6)

240 WHITE CLAY - Cone 6 (Photo C/6)

A very smooth, plastic throwing body. Suggested bisque temperature C/04. Shrinkage: 13% at C/6. Absorption: 2.75% at C/6.

240G WHITE CLAY W/GROG - Cone 6 (Photo C/6)

240G WHITE CLAY W/GROG - Cone 6 (Photo C/6)

A very smooth, plastic throwing body with fine grog. Suggested bisque temperature C/04. Shrinkage: 12.5% at C/6. Absorption: 2.75% at C/6.

563 CREAMY WHITE STONEWARE CLAY - Cone 6 (Photo C/6)

563 CREAMY WHITE STONEWARE CLAY - Cone 6 (Photo C/6)

Smooth vitreous stoneware body. Contains no fire clay. Suggested bisque temperature C/04. Shrinkage: 14% at C/6. Absorption: 1.0% at C/6.

630 WHITE STONEWARE CLAY - Cone 6 (Photo C/6)

630 WHITE STONEWARE CLAY - Cone 6 (Photo C/6)

Contains fire clay and mullite which enhances thermal properties. Suggested bisque temperature C/04. Shrinkage at C/6:  13.0%. Absorption at C/6:  1.5%.

213 PORCELAIN CLAY

213 PORCELAIN CLAY

A white body formulated for cone 6 firing. Plastic, throwable clay. Suggested bisque temperature C/06. Shrinkage: 12% at C/6 Absorption: 1.7% at C/6 

551 V.P. PORCELAIN - Cone 6 (Photo C/6)

551 V.P. PORCELAIN - Cone 6 (Photo C/6)

Very plastic white porcelain. Good for throwing. Does not contain ball clay. Suggested bisque temperature C/06. Shrinkage: 13% at C/6. Shrinkage: 13% at C/6. Absorption: .3% at C/6.

365 ENGLISH PORCELAIN - Cone 6 (Photo C/6)

365 ENGLISH PORCELAIN - Cone 6 (Photo C/6)

Same as 257 but formulated to fire at a lower temperature. Suggested bisque temperature C/06. Shrinkage: 13.5% at C/6. Absorption: .60% at C/6.

181 WHITE STONEWARE - Cone 6-10 (Photo C/6 Oxidation)

181 WHITE STONEWARE - Cone 6-10 (Photo C/6 Oxidation)

A very smooth white stoneware body. Contains no fire clay. Suggested bisque temperature C/04. Shrinkage: 13% at C/6, 13.9% at C/10. Absorption: 2.8% at C/6, 1.7% at C/10.

181 WHITE STONEWARE - Cone 6-10 (Photo C/10 Oxidation)

181 WHITE STONEWARE - Cone 6-10 (Photo C/10 Oxidation)

A very smooth white stoneware body. Contains no fire clay. Suggested bisque temperature C/04. Shrinkage: 13% at C/6, 13.9% at C/10. Absorption: 2.8% at C/6, 1.7% at C/10.

181 WHITE STONEWARE - Cone 6-10 (Photo C/10 Reduction)

181 WHITE STONEWARE - Cone 6-10 (Photo C/10 Reduction)

A very smooth white stoneware body. Contains no fire clay. Suggested bisque temperature C/04. Shrinkage: 13% at C/6, 13.9% at C/10. Absorption: 2.8% at C/6, 1.7% at C/10.

182 WHITE STONEWARE - Cone 6-10 (Photo C/6 Oxidation)

182 WHITE STONEWARE - Cone 6-10 (Photo C/6 Oxidation)

Near white plastic stoneware body. Good for use with bright glazes. Available with and without fine grog. Suggested bisque temperature C/04. Shrinkage: 10.5% at C/6, 12% at C/10.  Absorption: 5.5% at C/6, 2.1% at C/10.

182 WHITE STONEWARE - Cone 6-10 (Photo C/10 Oxidation)

182 WHITE STONEWARE - Cone 6-10 (Photo C/10 Oxidation)

Near white plastic stoneware body. Good for use with bright glazes. Available with and without fine grog. Suggested bisque temperature C/04. Shrinkage: 10.5% at C/6, 12% at C/10.  Absorption: 5.5% at C/6, 2.1% at C/10.

182 WHITE STONEWARE - Cone 6-10 (Photo C/10 Reduction)

182 WHITE STONEWARE - Cone 6-10 (Photo C/10 Reduction)

Near white plastic stoneware body. Good for use with bright glazes. Available with and without fine grog. Suggested bisque temperature C/04. Shrinkage: 10.5% at C/6, 12% at C/10.  Absorption: 5.5% at C/6, 2.1% at C/10.

130 PORCELAIN CLAY - Cone 7-10 (Photo C/10 Oxidation)

130 PORCELAIN CLAY - Cone 7-10 (Photo C/10 Oxidation)

A white firing, high temperature plastic body. Very fine white porcelain grog enhances strength and throwability. Suggested bisque temperature C/06. Shrinkage: 10% at C/7, 12% at C/10. Absorption: .75% at C/7, .5% at C/10.

130 PORCELAIN CLAY - Cone 7-10 (Photo C/10 Reduction)

130 PORCELAIN CLAY - Cone 7-10 (Photo C/10 Reduction)

A white firing, high temperature plastic body. Very fine white porcelain grog enhances strength and throwability. Suggested bisque temperature C/06. Shrinkage: 10% at C/7, 12% at C/10. Absorption: .75% at C/7, .5% at C/10.

257 ENGLISH PORCELAIN - Cone 8-10 (Photo C/10 Oxidation)

257 ENGLISH PORCELAIN - Cone 8-10 (Photo C/10 Oxidation)

A porcelain body with a parian like quality. It is white, tight and translucent when thin. Contains no ball clay. Suggested bisque temperature C/06. Shrinkage: 13% at C/8, 15% at C/10. Absorption: 1% at C/8, .65% at C/10.

257 ENGLISH PORCELAIN - Cone 8-10 (Photo C/10 Reduction)

257 ENGLISH PORCELAIN - Cone 8-10 (Photo C/10 Reduction)

A porcelain body with a parian like quality. It is white, tight and translucent when thin. Contains no ball clay. Suggested bisque temperature C/06. Shrinkage: 13% at C/8, 15% at C/10. Absorption: 1% at C/8, .65% at C/10.

437 TROY PORCELAIN - Cone 9-13 (Photo C/10 Oxidation)

437 TROY PORCELAIN - Cone 9-13 (Photo C/10 Oxidation)

A versatile, plastic English kaolin body. It throws and takes glazes well, and can be used in reduction, wood, and salt firings. Translucent when thin; wide range of color/texture in long wood firings.  Suggested bisque temperature C/06. Shrinkage:  13% at Cone 10,  Absorption:  0.3 % at Cone 10. Sample was woodfired without glaze.

437 TROY PORCELAIN - Cone 9-13 (Photo Woodfired)

437 TROY PORCELAIN - Cone 9-13 (Photo Woodfired)

A versatile, plastic English kaolin body. It throws and takes glazes well, and can be used in reduction, wood, and salt firings. Translucent when thin; wide range of color/texture in long wood firings.  Suggested bisque temperature C/06. Shrinkage:  13% at Cone 10,  Absorption:  0.3 % at Cone 10. Sample was woodfired without glaze.

508 WOODFIRE STONEWARE CLAY - Cone 10+ (Photo C/10 Oxidation)

508 WOODFIRE STONEWARE CLAY - Cone 10+ (Photo C/10 Oxidation)

Extremely versatile clay body for throwing and handbuilding. Fires to a very light gray color. Works well in both woodfiring and reduction.  Suggested bisque temperature C/04. Shrinkage:  12% at Cone 10, Absorption:  1.5% at C/10. Sample was woodfired without glaze.